ENGAGE™ 8407

Category:	TPO (POE) , Polyolefin Elastomer
Manufacturer:	The Dow Chemical Company
Trademark:	ENGAGE™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7QKeg2_ENGAGE-8407.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ENGAGE™8407 polyolefin elastomer is an ethylene-octene copolymer, which has excellent performance in the fields of injection molding of industrial and consumer durable goods and compression molding of gaskets. ENGAGE 8407 endows products that need visual inspection with higher transparency, and can use hot runner molds for processing, which improves production efficiency. In addition, its lower density also helps to control resin costs and production costs, while also reducing the weight of the final product. After blending with polypropylene (PP) and polyethylene (PE), ENGAGE 8407 also has good impact resistance, especially suitable for application fields requiring high melt flow modification. Main features: pellets Excellent flow characteristics The impact resistance of polypropylene and polyethylene can be improved after addition Added talcum powder (untreated, 1 µm) Application field: injection molded industrial and consumer durable goods Impact modification

Message

ENGAGE™8407 polyolefin elastomer is an ethylene-octene copolymer, which has excellent performance in the fields of injection molding of industrial and consumer durable goods and compression molding of gaskets.

ENGAGE 8407 endows products that need visual inspection with higher transparency, and can use hot runner molds for processing, which improves production efficiency. In addition, its lower density also helps to control resin costs and production costs, while also reducing the weight of the final product. After blending with polypropylene (PP) and polyethylene (PE), ENGAGE 8407 also has good impact resistance, especially suitable for application fields requiring high melt flow modification.

Main features:

pellets

Excellent flow characteristics

The impact resistance of polypropylene and polyethylene can be improved after addition

Added talcum powder (untreated, 1 µm)

Application field:

injection molded industrial and consumer durable goods

Impact modification

General Information
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.870	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	30	g/10 min	ASTM D1238
Mooney Viscosity (ML 1+4, 121°C)	2	MU	ASTM D1646

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shore A, 1 second, molded	72	ASTM D2240
Shore D, 1 second, molded	20	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Break, Compression Molded)	3.30	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	1000	%	ASTM D638
Flexural Modulus - 2% Secant (Compression Molded)	12.1	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-54.0	°C	Internal method
Vicat Softening Temperature	41.0	°C	ASTM D1525
Melting Temperature (DSC) ³	60.0	°C	Internal method

Additional Information
对无滑石粉产品测量的属性。

Note Message
1 .	510 mm/min
2 .	510 mm/min
3 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Sevrene® 3500-70A	Vi-Chem Corporation	TPE	Sevrene®
Sylvin 8324-60 White 1511	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Terblend® N NG-02	INEOS Styrolution Group GmbH	ABS+Nylon	Terblend® N
KOPA® KN333HFBL	Kolon Plastics, Inc.	Nylon 66	KOPA®
CP PRYME® Polypropylene PPC100SC-35M Clear CB	Chase Plastics Services Inc.	PP Copolymer	CP PRYME® Polypropylene