TECHNYL STAR® S 218 MT40 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NyIv2m_TECHNYLSTARS218MT40NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL STAR® S 218 MT40 Natural is based on a patented high flow polyamide 6 resin (TechnylStar), reinforced with 40% mineral filler, heat stabilized, for injection moulding. This grade offers good mechanical properties and is characterized by a high fluidity of the melt. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.45 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.72 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 2400 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield, 23°C | 75.0 | 55.0 | MPa | ASTM D638 |
| Fracture, 23°C | 7.00 | 22.0 | MPa | ASTM D638 |
| Fracture, 23°C | 90.0 | 55.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 8.0 | 34 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5500 | 1850 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | 65.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ||||
| 23°C | 120 | 100 | kJ/m² | ISO 179/1eU |
| 23°C | 150 | 330 | kJ/m² | ISO 179/1fU |
| Notched Izod Impact (23°C) | 5.0 | 8.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 100 | 245 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 100 | 200 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 186 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 90.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 - 235 | °C | |
| Middle Temperature | 235 - 245 | °C | |
| Front Temperature | 245 - 250 | °C | |
| Mold Temperature | 60 - 90 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 131 HF | RTP Company | PP, Unspecified | RTP |
| RTP EMI 361 FR | RTP Company | PC | RTP |
| Ferro PP TPP40AJ38BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| ELASTOSIL® P 7630 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| Kemcor LD 1333 | Qenos Pty Ltd | MDPE | Kemcor |