NOVALAC RX®660 Datasheet,Phenolic,Vyncolit N.V.-SHANGHAI SUSHENG

Message
RX®660 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type MFH.

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Ultra high toughness Good dimensional stability Low smoke High strength Antibacterial property Solvent resistance Good creep resistance alkali resistance acid resistance
Uses	Membrane key switch Pump parts Gear Electrical/Electronic Applications Electrical appliances Power/other tools Connector Application in Automobile Field Shell
Agency Ratings	ASTM D 5948, Type MFH
Appearance	Black Green
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.81	g/cm³	ISO 1183
Molding Shrinkage - Flow	0.20	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.060	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (E-Scale)	85		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break, Compression Molded)	70.0	MPa	ISO 527-2
Flexural Modulus (Compression Molded)	17000	MPa	ISO 178
Flexural Stress	120	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	2.7	kJ/m²	ISO 180
Unnotched Izod Impact Strength	5.7	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	200	°C	ISO 75-2/A
Linear thermal expansion coefficient			ASTM E831
Flow	2.3E-5	cm/cm/°C	ASTM E831
Lateral	2.7E-5	cm/cm/°C	ASTM E831
Thermal Conductivity	0.69	W/m/K	ASTM C177
RTI Elec	180	°C	UL 746
RTI Imp	180	°C	UL 746
RTI	180	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.6E+13	ohms	IEC 60093
Volume Resistivity	5.0E+13	ohms·cm	IEC 60093
Dielectric Strength (1.00 mm)	25	kV/mm	IEC 60243-1
Arc Resistance	180	sec	ASTM D495

Flammability	Nominal Value	Test Method
Flame Rating		UL 94
1.59 mm	V-0	UL 94
3.18 mm	V-0	UL 94

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Injection Pressure	100 - 248	MPa
Holding Pressure	30.0 - 89.6	MPa
Back Pressure	4.83 - 15.2	MPa

Injection instructions
Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167.All ASTM properties listed were tested in accordance with ASTM D5948.The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.Powder Density, ISO 60: 0.9 g/cm³HDT A (1.80 MPa) Unannealed, ISO 75A, Post Baked: >282°CCompressive Strength, ISO 604: 270 MPa

Injection instructions

Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167.All ASTM properties listed were tested in accordance with ASTM D5948.The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.Powder Density, ISO 60: 0.9 g/cm³HDT A (1.80 MPa) Unannealed, ISO 75A, Post Baked: >282°CCompressive Strength, ISO 604: 270 MPa

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	NOVALAC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7MvisV_NOVALAC-RX-660.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
POLYTROPE® STR 1030EU-01 NATURAL	A. Schulman Inc.	Polyolefin, Enhanced TPO	POLYTROPE®
Wondel® P PM6	Nanjing Julong Engineering Plastics Co., LTD	PP, Unspecified	Wondel® P
NEXUS ABS ABS405	Nexus Resin Group, LLC.	ABS	NEXUS ABS
Caltex PP MU40	GS Caltex	PP, Unspecified	Caltex PP
Osterlene® LD02520SA	Osterman & Company	LDPE	Osterlene®