EVATHENE® UE633
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | USI Corporation |
| Trademark: | EVATHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6sfoC7_EVATHENE-UE633.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVATHENE UE633 is an ethylene-vinyl acetate copolymer (EVA) resins designed for injection molding and extrusion coating. The most distinguished characteristic of EVATHENE UE633 is its strong resistance to stress cracking.UE633 is most ideal for making swimming fin, closure, bicycle handle, knife holder etc. All these products need softness and anticracking properties. UE633 can also be mixed with tackifier and low molecular weight LDPE to make hot melt to be used as instant adhesive for corrugated container. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 19.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 790 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 60.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 83.0 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 281D | RTP Company | Nylon 612 | RTP |
| Sinelec CCB5834 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinelec |
| TufCoat™ 6000 | Lucite International Inc. | Acrylic (PMMA) | TufCoat™ |
| Hostalen PP H2450 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| EPALINE 386A51 | Epaflex Polyurethanes S.R.L. | TPU, Unspecified | EPALINE |