LNP™ THERMOCOMP™ KB006 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Lp5dK_LNP-THERMOCOMP-KB006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KB006 is a compound based on Acetal containing 30% Glass Bead. Also known as: LNP* THERMOCOMP* Compound KB-1006 Product reorder name: KB006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 4.0 | % | |
| Across Flow : 24 hr | 1.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break 1 | 34.0 | MPa | ASTM D638 |
| Break | 37.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 2 | 20 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 4000 | MPa | ASTM D790 |
| -- 4 | 4320 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 65.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 5 | 43.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D4812 |
| 23°C 7 | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 155 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 152 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 107 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID D 300 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 612 | MAZMID D |
| New-prene™ 9165N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| ALTECH® PA6 A 2015/109 GF15 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Clariant PBT PBT-1700G30 | Clariant Corporation | PBT | Clariant PBT |
| Elastollan® 1185AF001 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |