| High heat injection molding grade of PMMA |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.7 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3 | 3100 | MPa | ASTM D790 |
| Flexural Strength 4 | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 102 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 210 to 232 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 221 to 243 | °C | |
| Nozzle Temperature | 216 to 238 | °C | |
| Processing (Melt) Temp | 221 to 243 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.689 to 1.38 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 303 TFE 15 FR | RTP Company | PC | RTP |
| RTP 882 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| Techsil RTV2410 | Techsil Limited | Silicone | Techsil |
| WELLAMID Nylon 6000 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ASI POLYPROPYLENE PP 3500 Natural | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |