TAROMID B 280 G2 X0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7CZ5Bc_TAROMID-B-280-G2-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 medium viscosity 10% glass fibres reinforced, flame retardant UL94 V0, heat stabilized, good flame proofing also at low thickness, good flow and good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 - 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.75 - 0.95 | % | Internal method |
| Flow direction | 0.45 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | ISO 62 |
| Saturated, 23°C | 7.0 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(850°C) | 10 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 5600 | MPa | ISO 178 |
| Flexural Stress 4 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.2 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 165 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 6 | 110 | °C | IEC 60216 |
| -- 7 | 130 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 208 | °C | ISO 306/A50 |
| -- | 202 | °C | ISO 306/B50 |
| Ball Pressure Test (170°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 20,000 hr |
| 7 . | Short term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ VS-693.G001-8009 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| SHIN-A SE-5000MPM70 | SHIN-A T&C | Epoxy | SHIN-A |
| Sindustris PP H7601 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Yanshan PE LD166 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Sylvin 8200-85 Black 293 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |