TOTAL Polyethylene EVA 1005 VN 2
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7ALyat_TOTAL-Polyethylene-EVA-1005-VN-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA 1005 VN 2 is made by a high pressure tubular process. Grade for transparent and resistant films. Application examples : Stretch, coextrusion, frozen food, agricultural film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 0.925 | g/cm³ | ISO 1183 |
| -- | 925 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Melt volume-flow rate (190°C/2.16 kg) | 0.700 | cm³/10min | ISO 1133 2 |
| Vinyl Acetate Content | 5.5 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 160 | MPa | ISO 527-2 |
| -- | 140 | MPa | ISO 527-2 3 |
| Tensile Stress (Yield) | 9.00 | MPa | ISO 527-2 4 |
| Tensile Strain (Yield) | 25 | % | ISO 527-2 5 |
| Tensile Elongation at Break | > 50 | % | ISO 527-2 6 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 9.50 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 8.50 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 32.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 27.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 570 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 340 | g | ISO 7765-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 90.0 | °C | ISO 306 |
| 50°C/h, B (50N) | 87.0 | °C | ISO 306 7 |
| Melting Temperature (DSC) | |||
| -- | 104 | °C | ISO 3146 |
| -- 8 | 104 | °C | ISO 11357-3 9 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Elmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 34 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 33 N/mmHaze, ISO 14782, Blown Film, 40 µm: 8.8% |
| Extrusion instructions |
|---|
| Advised Temperature Profile: 160 to 190°CPossible Range of Thicknesses: 45 to 300 µ |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | 10 °C/min |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Anjaconduct® 150-FR/KF1E6 | Almaak International GmbH | PC | Anjaconduct® |
| Infino LF-1030 | SAMSUNG SDI CO., LTD. | PC | Infino |
| Karina CLEAR PVC COMPOUND -E 80/230-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 105951-35/1-A-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Orgalloy® LT 4060 | Arkema | Nylon 6 Alloy | Orgalloy® |