Adell Polyamide AT-13
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 71lMLA_Adell-Polyamide-AT-13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adell Polyamide AT-13 is a Polyamide 66 (Nylon 66) material filled with 13% glass fiber. It is available in North America. Important attributes of Adell Polyamide AT-13 are:
Typical application of Adell Polyamide AT-13: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 to 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 84 | ||
| R-Scale | 119 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Compressive Strength | 124 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 229 | °C | |
| 1.8 MPa, Unannealed | 221 | °C | |
| Melting Temperature | 249 to 260 | °C | ASTM D789 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Softell CA7469A | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| Moplen HP648S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Ateva® 1641 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Neoflex™ 7060 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |
| Edgetek™ ET6000-5009 NHFR White VN-3902 | PolyOne Corporation | Nylon 6 | Edgetek™ |