Lumid® HI2202B(W)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ySAhM_Lumid-HI2202B-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumid®HI2202B(W) is a polyamide 66 (nylon 66) material, which contains a 20% glass fiber reinforced material. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lumid®The main characteristics of HI2202B(W) are: impact resistance. Lumid®The typical application field of HI2202B(W) is: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 127 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4900 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 250 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 230 | °C | ASTM D648 |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 4.00 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 265 - 275 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 270 - 285 | °C | |
| Nozzle Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.09% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RXD110 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Sindustris PBT TE5101 | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| TARODUR 100 TR | Taro Plast S.p.A. | ABS | TARODUR |
| DOW™ LDPE 7010E | The Dow Chemical Company | LDPE | DOW™ LDPE |
| ICORENE® N9203 | ICO Polymers EMEA, A Division of A. Schulman | PETG | ICORENE® |