DOWLEX™ GM 8071G
| Category: | LLDPE , Experimental Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rfgcic_DOWLEXGM8071G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ GM 8071G Polyethylene Resin is designed for use in a wide variety of film applications, in special for high strength consumer trash bags/liners. This product can be used in other applications that require toughness and also offers great melt strength for high throughput rates. Main Characteristics
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Puncture Resistance | 13.4 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD | 171 | MPa | ASTM D882 |
| 2% secant, TD | 187 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 9.38 | MPa | ASTM D882 |
| TD : Yield | 9.38 | MPa | ASTM D882 |
| MD : Fracture | 29.1 | MPa | ASTM D882 |
| TD : Fracture | 20.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 420 | % | ASTM D882 |
| TD : Fracture | 500 | % | ASTM D882 |
| Dart Drop Impact | 670 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 330 | g | ASTM D1922 |
| TD | 490 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 118 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.3 µm) | 45 | ASTM D2457 | |
| Haze (20.3 µm) | 17 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Machine: Monolayer blown film extrusion line Monolayer Film (0.9mil) Screw Size: 2.5 inch (63.5 mm) 30:1 L/D Screw Type: DSBII Die Gap: 70 mil Output: 10 lbs/hr./in. of die circumference Die Diameter: 8 in. Blow-up Ratio: 2.5 : 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-276 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| Silopren® Electro 1700 | Momentive Performance Materials Inc. | Rubber | Silopren® |
| Nanjing Hongrui PA66 A3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| CALSIN SE102 | Pooya Polymer Tehran | Polyolefin, Unspecified | CALSIN |
| Hostacom TRC 364N G82732 | LyondellBasell Industries | PP Copolymer | Hostacom |