TROSIFOL® Solar R40 Ultra White
| Category: | PVB , Polyvinyl Butyral |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | TROSIFOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6uZclD_TROSIFOL-Solar-R40-Ultra-White.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TROSIFOL® Solar R40 Ultra White is a Polyvinyl Butyral (PVB) material. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | DIN 53479 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 70 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 23.0 | MPa | ISO 527-3 |
| Tensile Elongation (Break) | > 250 | % | ISO 527-3 |
| Adhesion to Glass 1 | > 16.0 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1850 | J/kg/°C | ISO 11357-4 |
| Thermal Conductivity | 0.22 | W/m/K | EN 12664 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 2(23°C) | 1.0E+14 | ohms·cm | IEC 60093 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 3 | < 1.0 | % | EN 410 |
| Note Message | |
|---|---|
| 1 . | Compressive Shear Strength |
| 2 . | At 0.5% H2O content |
| 3 . | LSG made of 2 x 3 mm low-iron glass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP1B10 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Royalene® 868XE | Lion Copolymer, LLC | EPDM | Royalene® |
| TECHNYL® C 216 V35 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| NOVALAC RX®431 | Vyncolit N.V. | Phenolic | NOVALAC |
| Iupilon® FPR3500 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |