NOVALAC FM 3000
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | NOVALAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6iGHxY_NOVALAC-FM-3000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 3000 is a self-lubricated cellulose reinforced phenolic molding compound, modified for applications requiring reduced friction and low wear. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 38.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 7000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 55.0 | MPa | ASTM D790 |
| Compressive Strength | 105 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 180 | °C | ASTM D648 |
| CLTE - Flow | 2.6E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 10 | kV/mm | ASTM D149 |
| -- 2 | 7.9 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ASTM properties listed were tested in accordance with ASTM D5948.Powder Density, ASTM D1895: 0.45 g/cm³Water Absorption, ASTM D570, 48 hrs, 50°C: 1.2%Dielectric Strength, ASTM D149, 60 Hz, Method B, wet: 7.9 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 10.2 kV/mm |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANTEX® 672B | Nantex Industry Co., Ltd. | NBR | NANTEX® |
| ALCUDIA® LDPE 2321FS | REPSOL | LDPE | ALCUDIA® LDPE |
| KOPLA PP KPT1040 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |
| OLEFISTA™ QM4301E/QCM292 | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |
| Sylvin 7011EE-60 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |