ELITE™ 5220B
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vYhGcg_ELITE-5220B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™ 5220B is an Enhanced Polyethylene Resin material. It is available in Latin America. Typical application of ELITE™ 5220B: Food Contact Applications |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.915 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Resistance (20 µm) | 27.0 | J/cm³ | Internal Method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 15.0 | MPa | |
| TD : Yield, 20 µm | 17.0 | MPa | |
| MD : Break, 20 µm | 40.0 | MPa | |
| TD : Break, 20 µm | 36.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 680 | % | |
| TD : Break, 20 µm | 830 | % | |
| Dart Drop Impact (20 µm) | 820 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 390 | g | |
| TD : 20 µm | 600 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm) | 96 | ASTM D2457 | |
| Haze (20.0 µm) | 1.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 271 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 287 A TFE 10 SI 2 | RTP Company | Nylon 6 | RTP |
| Tecomid® NB40 NL RM | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Hipolyene 8515 TY | Zylog Plastalloys | TPO (POE) | Hipolyene |
| MAJ'ECO EN030LA | AD majoris | Biodeg Polymers | MAJ'ECO |
| Medalist® MD-555 | Teknor Apex Company | TPE | Medalist™ |