RTP ESD 2181
| Category: | PEI , Polyether Imide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6WGXtf_RTP-ESD-2181.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber - ESD Protection |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Moisture Content | 0.040 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8620 | MPa | ASTM D638 |
| Tensile Strength | 157 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 231 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 510 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 207 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+9 | ohms | ASTM D257 |
| Volume Resistivity | < 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 354 - 399 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMNO P40 TLD | Arkema | Nylon 11 | Rilsan® |
| THERMOLAST® K TF7BNA (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Andur AL 62 DP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Lupoy庐 GN5009F | LG Chem Ltd. | PC+ABS | Lupoy® |
| LNP™ THERMOCOMP™ DF0049 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |