MAJORIS GC119 - 1367

Category:	PP, Unspecified , Polypropylene
Manufacturer:	AD majoris
Trademark:	MAJORIS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6PPh4u_MAJORIS-GC119---1367.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

GC119 - 1367 is a mineral filled polypropylene compound intended for injection moulding.

The product is available in white (GC119 - 1367) and natural (GC119) but other colours can be provided on request.

The good flow ability of GC119 - 1367 makes it very easy to process even for complicated parts. The material displays excellent gloss, very low dust pick up and is high heat stabilised.

APPLICATIONS

Household articles

Electrical appliances

Technical components

GC119 - 1367 is intended for components, which require very good surface quality, rigidity, good impact, low shrinkage and high dimensional stability.

General Information
Filler / Reinforcement	Mineral filler, 10% filler by weight
Additive	heat stabilizer
Features	Good dimensional stability Rigidity, high Highlight Impact resistance, good Recyclable materials Workability, good Good liquidity Heat resistance, high Thermal Stability Low shrinkage Good appearance Excellent appearance
Uses	Electrical/Electronic Applications Electrical appliances Household goods
Appearance	White Available colors Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.980	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	22	g/10 min	ISO 1133
Molding Shrinkage	1.6	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress			ISO 527-2/50
Yield	30.0	MPa	ISO 527-2/50
Fracture	24.0	MPa	ISO 527-2/50
Flexural Modulus ¹	1950	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	98.0	°C	ISO 75-2/B

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	3.0	hr
Processing (Melt) Temp	220 - 260	°C
Mold Temperature	30.0 - 50.0	°C
Injection Rate	Moderate

Injection instructions
Holding pressure: 50 to 70% of the injection pressure

Note Message
1 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
Maxxam™ MN-818.T001-8001	PolyOne Corporation	PP, Unspecified	Maxxam™
RTP 2203 LF TFE 20	RTP Company	PEEK	RTP
Telcar® TL-1996E NAT	Teknor Apex Company	TPE	Telcar®
Cri-Line HFLT-720-75	Cri-Tech, Inc.	Fluorelastomer	Cri-Line
HANWHA LLDPE HS1700	Hanwha Chemical	LLDPE	HANWHA LLDPE