Thermx® CG923
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Thermx® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6BbHsy_Thermx-CG923.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermx® CG923 is a 20% glass fiber reinforced and flame retardant polycyclohexylenedimethylene terephthalate for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 7200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 235 | °C | ISO 75-2/A |
| Melting Temperature 1 | 285 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Processing (Melt) Temp | 295 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 20 | RTP Company | Nylon 66 | RTP |
| Quadraflex™ ARE-95A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Sinvicomp SBB3704 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| LUBEMID B27 GF30 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| LUVOCOM® 1880-8749 | Lehmann & Voss & Co. | LCP | LUVOCOM® |