Retpol® 3011 HS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6AyEhb_Retpol-3011-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron 3011 HS is a 45% glass fibre reinforced coupled polypropylene compound. It is a medium to high flow injection moulding grade developed for components requiring excellent creep resistance with high heat deflection temperatures, very high rigidity and good impact strength. It has been stabilized to meet automotive heat aging requirements of 21days at 150°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.10 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 111 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 84 | ||
| Shore D, 15 sec, 3.00 mm | 78 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 120 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 9300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 620 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 152 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen Z11G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| KumhoSunny PC HCG2520MP | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| LubriOne™ AT-000/18T 2S | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| Plenco 02308 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |
| TOTAL Polyethylene Lumicene® M 3581 UV (US) | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |