LubriOne™ AT-000/18T 2S
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VDX0po_LubriOne-AT-000-18T-2S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.0 to 3.0 | % | |
| Across Flow | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1770 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 2 | 40.0 | MPa | |
| Break 3 | 40.0 | MPa | |
| Tensile Elongation 4(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 5 | 1740 | MPa | ASTM D790 |
| Flexural Strength 6 | 62.7 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.10 | ||
| vs. Steel - Static | 0.14 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 37 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 151 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 81.1 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | 5.1 mm/min |
| 4 . | Type I, 5.1 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT SIGNATURE CAP MG-100 | NEXT Specialty Resins, Inc. | CAP | NEXT SIGNATURE |
| LUVOCOM® 19-7330 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| Daelim Po1y® XP9500M | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |
| Sylvin 4200-80UV Grey 9539 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2946-73 Clear 8422 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |