Toyolac® 600-X06
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 68Aiso_Toyolac-600-X06.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toyolac® 600-X06 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 50.0 | MPa | ASTM D638 |
| 23°C | 57.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 64 | % | ASTM D638 |
| Break, 23°C | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2230 | MPa | ASTM D790 |
| 23°C | 2360 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 74.0 | MPa | ASTM D790 |
| 23°C | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 21 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C, 12.7 mm) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 to 95.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2655 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Badamid® LB70 GF M45 FR HF | Bada AG | Nylon 6 | Badamid® |
| KumhoSunny ABS HU650 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Lumid® GN2251BF | LG Chem Ltd. | Nylon 66 | Lumid® |
| ADENE® N09CTE-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |