Electrafil® PC 04008
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 66HG8C_Electrafil-PC-04008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®PC 04008 is a polycarbonate (PC) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.35 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 75.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus | 3930 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 146 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 141 | °C | ASTM D648 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 10 - 1.0E+3 | ohms·cm | ASTM D257 |
| Static Decay | FTMS 101B | ||
| Shielding Effectiveness - 30 to 1000 MHz | 45 | dB | ASTM D4935 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 302 - 316 | °C | |
| Middle Temperature | 316 - 332 | °C | |
| Front Temperature | 310 - 327 | °C | |
| Nozzle Temperature | 310 - 327 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PA523G15 | Guangdong Silver Age Sci & Tech. Co., Ltd | Nylon 6 | SILVER® |
| Tecnoflon® PFR 94 | Solvay Specialty Polymers | Perfluoroelastomer | Tecnoflon® PFR |
| TITANEX® HM4560UA | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANEX® |
| ESTABLEND PC ABS 4502 V0 | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| Karina IVORY PVC COMPOUND 105900-35/ 1-B-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |