LNP™ LUBRICOMP™ Lexan_LF0335 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Z7nfZ_LNP-LUBRICOMP-Lexan-LF0335-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP LEXAN_LF0335 compound is a 35% glass fiber, milled glass reinforced PC injection moulding resin with improved wear resistance and reduced friction. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 260°C/5.0 kg | 11.0 | cm³/10min | |
| 300°C/1.2 kg | 9.00 | cm³/10min | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.23 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1 | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Unnotched Izod Impact Strength 2 | ISO 180/1U | ||
| -30°C | 38 | kJ/m² | |
| 23°C | 34 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 141 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 136 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.4E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FHR EPS 55-5655 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| 3M™ Dyneon™ Fluoroelastomer FX 2530R | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Electrafil® PC 04004 FR BK | Techmer Engineered Solutions | PC | Electrafil® |
| GERMADUR HSZ | Kunststoff-Kontor-Hamburg GmbH | PBT | GERMADUR |
| EMPILON® HC41 | EMPILON | SEBS | EMPILON® |