ColorFast® ACR100IM
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5OS8wS_ColorFast-ACR100IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact version, extrusion or injection molding PMMA |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 45 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 35 | % | |
| Flexural Modulus 3 | 1860 | MPa | ASTM D790 |
| Flexural Strength 4 | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 79.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 210 to 232 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 221 to 243 | °C | |
| Nozzle Temperature | 216 to 238 | °C | |
| Processing (Melt) Temp | 221 to 243 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.689 to 1.38 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V525MI12 | Lucent Polymers, Inc. | PP, Unspecified | Primefin |
| Shinko-Lac® ABS 3302 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| KumhoSunny PC/PBT HCB9310G | Shanghai KumhoSunny Plastics Co., Ltd. | PC+PBT | KumhoSunny PC/PBT |
| LNP™ COLORCOMP™ M1000S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ COLORCOMP™ |
| Osterlene® HI-8-2-hg | Osterman & Company | PS (HIPS) | Osterlene® |