Jamplast JPLGABSE
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5MCZDS_Jamplast-JPLGABSE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Jamplast ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes. The sheet and thermoforming grades of Jamplast ABS resins provide excellent high and low gloss aesthetics, thermal color stability, heat and impact resistance and stiffness for applications such as luggage, tool cases, burial vault liners, signs and recreation vehicles. Jamplast ABS resins can fill a variety of needs by offering ranges in melt flow rates from 1.0 to 4.0 g/10 min., sheet Izod impacts from 2.5 to 10.5 ft-lb/in and sheet flexural modulus from 285,000 to 300,000 psi. This resin is the lowest gloss and highest melt flow rate option of our ABS sheet grades. With a melt flow rate of 4.0 g/10 min., JPLGABSE can be used for low gloss, low impact applications where easy processability is desired. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.9 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| L-Scale | 80 | ||
| R-Scale | 108 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1860 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 30.3 | MPa | |
| Break | 31.7 | MPa | |
| Tensile Elongation 3(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 4 | 2210 | MPa | ASTM D790 |
| Flexural Strength 5 | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -18°C, 3.18 mm 6 | 80 | J/m | |
| 23°C, 3.18 mm 7 | 130 | J/m | |
| Gardner Impact | ASTM D3029 | ||
| -18°C, 2.54 mm | 19.8 | J | |
| 23°C, 2.54 mm | 22.6 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 96.1 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 218 to 274 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 3.45 | MPa | |
| Clamp Tonnage | 2.8 to 6.9 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 3.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | 0.25 mm Notch Depth |
| 7 . | 2.5E-3 mm Notch Depth |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 TFE 18 SI 2 | RTP Company | PBT | RTP |
| Sevrene® 6750-70A | Vi-Chem Corporation | TPE | Sevrene® |
| Tarnamid® T- 27 GF30 TF15 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| AKROMID® B3 GF 47 1 TM black (4936) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Evatane® 33-25 | Arkema | EVA | Evatane® |