Sumitomo Phenolic FM 3000
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Phenolic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Lf3h3_Sumitomo-Phenolic-FM-3000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 3000 is a self-lubricated cellulose reinforced phenolic molding compound, modified for applications requiring reduced friction and low wear. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Apparent Density | 0.45 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Water Absorption - 48 hr | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale, Compression Molded) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Compression Molded) | 38.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 7000 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 55.0 | MPa | ASTM D790 |
| Compressive Strength | 105 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 27 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 180 | °C | ASTM D648 |
| CLTE - Flow | 2.6E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 10 | kV/mm | |
| -- 3 | 7.9 | kV/mm |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE 1285 | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| NEFTEKHIM PE 6148C (486H3) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Ferro PP LPP30BC11BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Generic PC - Carbon Fiber, Nickel-Coated | Generic | PC | Generic |
| XYLEX™ X7509HP resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |