Order Products : sales@su-jiao.com
LEXAN™ FXD1413T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4tU6sl_LEXANFXD1413Tresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 9.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.40 - 0.80 | % | Internal method |
| Flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.13 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.096 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2270 | MPa | ASTM D638 |
| -- | 2310 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 60.0 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 66.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 6.0 | % | ASTM D638 |
| Yield | 5.6 | % | ISO 527-2/50 |
| Fracture 6 | 130 | % | ASTM D638 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2270 | MPa | ASTM D790 |
| -- 8 | 2190 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 91.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 87.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | ISO 179/1eA |
| 23°C | 70 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 800 | J/m | ASTM D256 |
| 23°C | 890 | J/m | ASTM D256 |
| -30°C 12 | 55 | kJ/m² | ISO 180/1A |
| 23°C 13 | 65 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 14 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 82.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 15 | 119 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525, ISO 306/B50 12 16 |
| -- | 143 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 95°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 95°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 7.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 217 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Nozzle Temperature | 288 - 310 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 71.0 - 93.0 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 80*10*4 mm |
| 16 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EB 0.24/45 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| TABOND 3045 | SILON s.ro | LLDPE | TABOND |
| Hipolyene 8015 FRC | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Durez® 33181 | SBHPP | Phenolic | Durez® |
| DAI-EL™ G-7401 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |