RELENE® 50GF003
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TFUkWQ_RELENE-50GF003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50GF003 is a blown film grade of High Molecular Weight High Density Polyethylene (HMHDPE). It possesses bimodel molecular weight distribution, which improves processability. 50GF003 can readily be processed on HMHDPE blown film extrusion lines. The films will have homogeneous, finely textured, opaque appearance and exhibit very good mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.30 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 20 µm | 31.0 | MPa | |
| TD : Yield, 20 µm | 32.0 | MPa | |
| MD : Break, 20 µm | 54.0 | MPa | |
| TD : Break, 20 µm | 51.0 | MPa | |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 20 µm | > 600 | % | |
| TD : Break, 20 µm | > 600 | % | |
| Dart Drop Impact 3 | 8.0 | g | ASTM D1709 |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 20 µm | 0.60 | g | |
| TD : 20 µm | 9.2 | g |
| Note Message | |
|---|---|
| 1 . | 20 µm film made with 0.75mm die gap & 4 BUR |
| 2 . | 20 µm film made with 0.75mm die gap & 4 BUR |
| 3 . | F50, 38mm dart, 66cm height |
| 4 . | 20 µm film made with 0.75mm die gap & 4 BUR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-571U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Multi-Flex® TPO 1047 S | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| Multiuse Leostomer® LE-3150N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Abstron SHF50+ | Bhansali Engineering Polymers Limited | ABS | Abstron |
| TECHNYL® A 218C V10 NATURAL S | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |