Alcryn® 2250 UT
| Category: | MPR , Melt Processable Rubber |
| Manufacturer: | Advanced Polymer Alloys |
| Trademark: | Alcryn® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4qEP9g_Alcryn-2250-UT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Alcryn® 2250 UT is a Melt Processable Rubber (MPR) material. It is available in Asia Pacific, Europe, or North America for blow molding, extrusion, injection molding, or vacuum forming. Important attributes of Alcryn® 2250 UT are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D471, ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 1.90 mm, Compression Molded) | 47 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 5.00 | mg | ASTM D1044 |
| Torsion Modulus 1 | ASTM D1043 | ||
| -20°C, 1.90 mm | 2.60 | MPa | |
| 24°C, 1.90 mm | 1.90 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set 2 | 7 | % | ASTM D412 |
| Tensile Stress | |||
| 100% Strain, 1.90 mm 3 | 1.90 | MPa | ASTM D412, ISO 37 |
| 100% Strain, 125°C, 1.90 mm 4 | 1.60 | MPa | ASTM D573, ISO 188 |
| Tensile Strength | |||
| Yield, 1.90 mm 5 | 6.80 | MPa | ASTM D412, ISO 37 |
| Yield, 125°C, 1.90 mm 6 | 6.40 | MPa | ASTM D573, ISO 188 |
| Tensile Elongation | |||
| Break, 125°C, 1.90 mm 7 | 450 | % | ASTM D573, ISO 188 |
| Break, 1.90 mm 8 | 420 | % | ASTM D412, ISO 37 |
| Tear Strength (1.90 mm) | 19.2 | kN/m | ASTM D624 |
| Compression Set 9 | ASTM D395B, ISO 815 | ||
| 24°C, 22 hr | 15 | % | |
| 100°C, 22 hr | 56 | % | |
| Clash-Berg Modulus (-26°C) | 68.9 | MPa | ASTM D1043 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Durometer Hardness in Air 10(Shore A, 125°C, 168 hr) | -2.0 | ASTM D573, ISO 188 | |
| Change in Volume 11 | |||
| 27°C, 168 hr, in Reference Fuel B | 24 | % | ASTM D471, ISO 1817 |
| 100°C, 168 hr, in ASTM Oil #1 | -39 | % | ASTM D471 |
| 100°C, 168 hr, in IRM 903 Oil | 32 | % | ASTM D471, ISO 1817 |
| 100°C, 168 hr, in Water | 7.0 | % | ASTM D471, ISO 1817 |
| 100°C, 168 hr, in ASTM #1 Oil | -39 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -91.0 | °C | ASTM D746, ISO 812 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (190°C, 300 sec^-1) | 115 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 166 | °C |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 1.9 mm, Compression Molded |
| 3 . | Compression Molded |
| 4 . | 7 days, Compression Molded |
| 5 . | Compression Molded |
| 6 . | 7 days, Compression Molded |
| 7 . | 7 days, Compression Molded |
| 8 . | Compression Molded |
| 9 . | Type I pellets, 12.7 mm diameter, plied up from 1.9 mm slabs |
| 10 . | 1.9 mm, Compression Molded |
| 11 . | 1.9 mm, Compression Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8240-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Grilamid® TR 90 NZZ nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Hyril® SAN500 | Entec Polymers | SAN | Hyril® |
| INELEC ABSAS | Infinity LTL Engineered Compounds | ABS | INELEC |
| LG EPS R240 | LG Chem Ltd. | PS (EPS) | LG EPS |