Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
Manufacturer: | BASF Corporation |
Trademark: | Ultraform® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 4lfKfc_Ultraform-E3120-BM.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Material with high melt strength, -stiffness and high stretchability for producing extrusion blow-molded hollow objects. |
General Information | |
---|---|
Features |
|
Uses |
|
Agency Ratings |
|
RoHS Compliance |
|
Forms |
|
Processing Method |
|
Resin ID (ISO 1043) |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.41 | g/cm³ | ISO 1183 |
Apparent Density | 0.85 | g/cm³ | |
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 0.800 | cm³/10min | ISO 1133 |
Water Absorption | ISO 62 | ||
Saturation, 23°C | 0.80 | % | |
Equilibrium, 23°C, 50% RH | 0.20 | % |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Ball Indentation Hardness (H 358/30) | 135 | MPa | ISO 2039-1 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 2450 | MPa | ISO 527-2 |
Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
Tensile Strain (Yield) | 9.0 | % | ISO 527-2/50 |
Nominal Tensile Strain at Break | 25 | % | ISO 527-2/50 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 230 | kJ/m² | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
Melting Temperature | 164 | °C | ISO 11357-3 |
CLTE - Flow (23 to 55°C) | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
Maximum Service Temperature - short cycle operation | 100 | °C |
Additional Information | Nominal Value | Test Method | |
---|---|---|---|
ISO Type | POM-K, B-GNR, 01-002 | ISO 9988-1 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
Relative Permittivity (1 MHz) | 3.80 | IEC 60250 | |
Dissipation Factor (1 MHz) | 5.0E-3 | IEC 60250 | |
Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating (1.60 mm) | HB | UL 94 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 200 GB 30 HS | RTP Company | Nylon 66 | RTP |
RTP 205 HS MS | RTP Company | Nylon 66 | RTP |
MonoSol® F100 | MonoSol, LLC | CA | MonoSol® |
Nymax™ GF1200 A43 NC052 | PolyOne Corporation | Nylon 66 | Nymax™ |
HiFill® PA6 0137 S2 | Techmer Engineered Solutions | Nylon 6 | HiFill® |