Orevac® 18910
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Arkema |
| Trademark: | Orevac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8bPCxV_Orevac-18910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OREVAC® 18910 is a maleic anhydride modified linear low-density polyethylene available in pellet form. It can be processed on most extrusion equipments designed to process conventional polyolefins. Applications OREVAC® 18910 has been designed to develop a reliable bonding strength between PS, PE, EVOH and PA in coextruded multi-layer structures like films or sheets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238, ISO 1133 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 77.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 117 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 to 200 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 200 to 210 | °C | |
| Cylinder Zone 4 Temp. | 210 to 220 | °C | |
| Cylinder Zone 5 Temp. | 220 to 230 | °C | |
| Melt Temperature | < 250 | °C | |
| Die Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TPSF-G10 | Polymer Resources Ltd. | PBT | PRL |
| Miflon® 3112 | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| BITONER® TR-100 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Flontech® FT-EK5-CF5-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| POLYelast TPE ZC500 D40 | Polykemi AB | TPE | POLYelast |