CERTENE™ LDF-0218A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4kHAeR_CERTENE-LDF-0218A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-0218A is a certified prime grade specially designed for EXTRUSION of heavy duty Blown Film for industrial applications requiring excellent mechanical properties, such as heavy duty sacks, shipping bags, shrink wrapping pallet hoods, construction, agriculture and greenhouses. LDF-0218A features excellent processability and films exhibit high toughness, high impact and tear strength, and excellent shrink properties. LDF-0218A contains no antiblock, no UV stabilizer and no slip. LDF-0218A complies with FDA regulation 21CFR 177.1520 (c ) 2.1 + 2.2 and most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm | 172 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 10.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 9.65 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 24.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 24.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 130 | % | ASTM D882 |
| TD : Fracture, 51 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 320 | g | ASTM D1922 |
| TD : 51 µm | 150 | g | ASTM D1922 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 221 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-PF370 | Sumitomo Bakelite Co., Ltd. | Nylon, Unspecified | Sumikon® |
| Durez® 83537 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Globalene® 6331F | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Hifax CA45F | LyondellBasell Industries | TPO (POE) | Hifax |
| LUVOCOM® 21-8113 | Lehmann & Voss & Co. | Nylon 6/6T | LUVOCOM® |