NuSil EPM-2422

Category:	Silicone , Silicone
Manufacturer:	NuSil Technology
Trademark:	NuSil
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4dw14Z_NuSil-EPM-2422.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

As a low stress alternative for electronic packaging, NuSil Technology's silicones allow the designer to choose from a unique line of silicones for various levels of packaging. We have an extensive line of encapsulants, adhesives, and greases to choose from. These include thermally and electrically conductive silicones for Thermal Interface Materials (TIM) or for EMI and RFI shielding applications.

Benefits of Silicone for Electronics:

Wide Operating Temperature Range of -115 °C to 250 °C

Low moisture absorption, < 0.4% Typical

Corrosion Resistance

High Dielectric Strength > 500 V/mil (0.001 inch) or 20 kV/mm

Fillers can be added to provide thermal and electrical conductive properties

Low Modulus (Typically less than 5.5 MPa/800 psi)

Stable chemical and mechanical properties when exposed to high temperatures

Low Shrinkage

Available as gels, elastomers, film adhesives sheeting, and greases

General Purpose: Potting and Encapsulating Materials

Comments: 1.43 Refractive Index

General Information
Features	Good Corrosion Resistance Good Thermal Stability Low Moisture Absorption Low Shrinkage
Uses	Electrical/Electronic Applications
Processing Method	Encapsulating Potting

Thermal	Nominal Value	Unit
CLTE - Flow	4.9E-4	cm/cm/°C

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+15	ohms·cm	ASTM D257
Dielectric Strength	22	kV/mm	ASTM D149

Optical	Nominal Value
Refractive Index	1.430

Thermoset	Nominal Value	Unit
Thermoset Components
Part A	Mix Ratio by Weight: 10
Part B	Mix Ratio by Weight: 1.0

Additional Information	Nominal Value	Unit
Cure System	Platinum
Ionic Content
Cl	< 5	ppm
K	< 1	ppm
Na	< 1	ppm
Operating Temperature	-115 to 260	°C

Uncured Properties	Nominal Value	Unit
Color	Clear/Transparent
Density	1.04	g/cm³
Viscosity ¹	3.5	Pa·s
Curing Time (65°C)	4.0	hr

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	40
Lap Shear Strength ²	1.24	MPa
Tensile Strength	4.31	MPa
Tensile Elongation at Break	130	%

Note Message
1 .	Part A
2 .	Primed with CF1-135

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom PP5940 B2	Spartech Polycom	PP, Unspecified	Spartech
Ultraform® N 2650 Z4	BASF Corporation	Acetal (POM) Copolymer	Ultraform®
Generic PTT	Generic	PTT	Generic
OTECH TPO OTR8588 - Gasket	OTECH Corporation	TPE	OTECH TPO
Sylvin 8470-70 Blue 8377	Sylvin Technologies Incorporated	PVC+PUR	Sylvin