Safrene® F 7740F2
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | Safrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4QxnGH_Safrene-F-7740F2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Safrene® F 7740F2 High Density Polyethylene Resin is a medium molecular mass extrusion grade ideally suited to the extrusion and subsequent knitting of tapes and monofilaments typically used in agricultural pockets and shade netting. Safrene® F 7740F2 High Density Polyethylene Resin is also used for film extrusion applications where excellent roll geometry is required. As a film it exhibits an excellent barrier to moisture. Safrene® F 7740F2 High Density Polyethylene Resin contains slip and antistatic additives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.946 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.40 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 1.7 | g/10 min | ISO 1133 |
| Spiral Flow | 32.0 | cm | Internal method |
| Viscosity Number (Reduced Viscosity) | 270.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, molding | 21.0 | MPa | ISO 527-2/50 |
| Fracture, molding | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2/50 |
| Flexural Stress (3.5% Strain, Compression Molded) | 17.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C, molded | 8.0 | kJ/m² | ISO 179 |
| 23°C, molded | 15 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 73.0 | °C | ISO 306/B |
| Peak Crystallization Temperature (DSC) | 130 - 133 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 | °C | |
| Melt Temperature | 190 - 240 | °C | |
| Die Temperature | 210 - 220 | °C |
| Extrusion instructions |
|---|
| Film Extrusion Cconditions: Feed Zone: 170°C Die: 210 to 220°C Melt Temperature: 190 to 240°C |
| Note Message | |
|---|---|
| 1 . | Unannealed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-1200/30 NAT | Techmer Engineered Solutions | ABS | TES |
| Fiberfil® J-60/40/E/EX | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Foam-It® 26 | Smooth-On, Inc | PUR, Unspecified | Foam-It® |
| Hylon® N1013THLUV2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Formolene® HB6007F | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |