SCLAIR® 14G
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4HVv2X_SCLAIR-14G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SCLAIR®14G is a medium density polyethylene material,. This product is available in North America and is processed by film extrusion. SCLAIR®The main features of 14G are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.936 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.72 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.24 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 390 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 520 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 17.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 17.0 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 34.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 29.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 900 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 62 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 40 | g | ASTM D1922 |
| TD : 38 µm, blown film | 130 | g | ASTM D1922 |
| Oxygen Permeability 1(23°C, 38 µm, blown film) | 2300 | cm³/m²/24 hr | ASTM D1434 |
| Water Vapor Transmission Rate (38°C, 100% RH, 38 µm, Blown Film) | 5.2 | g/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (38.0 µm) | 240 | J/cm | Internal method |
| Extrusion instructions |
|---|
| Optimum Blow-up Ratio: 2:1 to 3:1Die Gap: 0.9 to 2.2 mm |
| Note Message | |
|---|---|
| 1 . | 0% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mineralblend® PP-3450 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Homopolymer | Mineralblend® |
| Thermec™ 4150R30 | Technical Polymers, LLC | PPS | Thermec™ |
| MARPOL® HDM 507 | Marco Polo International, Inc. | HDPE | MARPOL® |
| PSM® HL-303 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |
| Sylvin 9657-85 Clear Red 6266 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |