Karina IVORY PVC COMPOUND 951-35/ 4-IS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3zNuDR_Karina-IVORY-PVC-COMPOUND-951-35-4-IS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND WITH HIGH ELECTRICAL INSULATION RESISTANCE RECOMMENDED FOR INSULATION OF CI AND CCI CABLES. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.29 to 1.35 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -1.73 to 1.27 | ME 12 | |
| Color b | 7.91 to 10.9 | ME 12 | |
| Color L | 86.9 to 89.9 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 40 | % | NBR 9148 |
| Maximum Variation of Tensile Strength | < 20 | % | NBR 9148 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 15 sec | 92 to 96 | ||
| Shore D | 61 to 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 12.6 | MPa | NBR 9141 |
| Tensile Elongation (Yield) | > 130 | % | NBR 9141 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | NBR 9148 |
| Tensile Elongation 3(Break) | > 130 | % | NBR 9148 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 6.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 23 | % | NBR 6245 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 30YM240E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Epiall® 1961B-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Epiall® |
| Sylvin 8982-90 FUV Brown 7218 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Polidiemme® G/220 | Solvay Specialty Polymers | TSE | Polidiemme® |
| Sylvin 3210-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |