Talcoprene® C530 M8 NATURALE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Talcoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3vLmt5_Talcoprene-C530-M8-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Talcoprene® C530 M8 NATURALE is a Polypropylene material. It is available in Europe, Latin America, or North America for injection molding. Important attributes of Talcoprene® C530 M8 NATURALE are:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 1.1 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Ash Content | 30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 24.0 | MPa | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 57.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 70.0 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.40 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baypreg® F 310 (25 mm Glass Mat Reinforced Sandwich) | Covestro - PUR | PUR, Unspecified | Baypreg® |
| BP Flex D 4107 CU BLK | Buckeye Polymers, Inc. | TPO | BP Flex |
| Lucolast庐 7010 | Lucobit AG | EBA | Lucolast® |
| Sylvin 7833-85 Blue 8446 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SABIC® LLDPE 218B | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |