ELIX™ ABS HH 3114
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ELIX Polymers, S. L. |
| Trademark: | ELIX™ ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3cnyWY_ELIX-ABS-HH-3114.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Very high heat resistance ABS ISO shortname: ISO 2580-1 ABS 2-M, MG, 115-08-09-20 Benefits:
Chemical Composition:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.60 to 0.70 | % | |
| Flow | 0.60 to 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 105 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 42.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 17 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ISO 306/B50 |
| -- | 114 | °C | ISO 306/B120 |
| CLTE - Flow (23 to 55°C) | 9.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(2.00 mm) | < 55 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec | ISO 294 |
| Note Message | |
|---|---|
| 1 . | 60x60x2 |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | US - FMVSS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5508(f1) | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Vipel® F013-HHH-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Viton® B-600 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| HiFill® PA6 G/M40 L UV | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Plastiglas FG® | Plastiglas de Mexico S.A de C.V. | Acrylic, Unspecified | Plastiglas |