Celstran® PPS-CF30-01
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3VurkG_Celstran-PPS-CF30-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celstran PPS-CF30-01 is a 30% long carbon fiber reinforced polyphenylene sulfide. This material imparts excellent impact and extremlely high modulus properties that exceed that of short carbon fiber PPS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 31800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 203 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 0.72 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 30100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 339 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.7E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.0E-3 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 285 - 295 | °C | |
| Middle Temperature | 315 - 345 | °C | |
| Front Temperature | 315 - 345 | °C | |
| Nozzle Temperature | 315 - 345 | °C | |
| Processing (Melt) Temp | 315 - 335 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 315 to 345°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 203-40 | ExxonMobil Chemical | TPV | Santoprene™ |
| Moplen RP210R | PolyMirae | PP Random Copolymer | Moplen |
| NaturePlast NP WF 004 | NaturePlast | Biodeg Polymers | NaturePlast |
| KRYSTALGRAN™ PE192-100 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALGRAN™ |
| Lupoy® GN1002FH | LG Chem Ltd. | PC | Lupoy® |