RTP EMI 660.75
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3AH1Fz_RTP-EMI-660-75.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Moisture Content | 0.10 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 7.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 - 8.0 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 270 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+5 | ohms | ASTM D257 |
| -- | < 1.0E+4 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 204 - 246 | °C | |
| Mold Temperature | 65.6 - 82.2 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6331 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Unipren® Elastomers B3 PRTA010 75A UP318 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| AKROMID® A3 GM 15/15 black (1073) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| 3M™ Dyneon™ PTFE Compound TF 8914 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Sylvin 3240-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |