ALCUDIA® LDPE PE046
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2zwYY5_ALCUDIA-LDPE-PE046.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® PE046/A is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown or cast film applications. This material offers easy processability, good balance of slip, mechanical and optical properties and excellent draw down. It contains slip and antiblock additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 150 to 180°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | < 0.10 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 30 µm, blown film | 10.0 | MPa | ISO 527-3 |
| TD : Yield, 30 µm, blown film | 10.0 | MPa | ISO 527-3 |
| MD : Broken, 30 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 30 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 30 µm, blown film | 200 | % | ISO 527-3 |
| TD : Broken, 30 µm, blown film | 550 | % | ISO 527-3 |
| Dart Drop Impact (30 µm, Blown Film) | 90 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 30 µm, blown film | 3.5 | N | ISO 6383-2 |
| TD : 30 µm, blown film | 1.3 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 30 µm thickness film, blow up ratio 2.25:1, frost line height 40 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA U407 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Andur 8 APLF/Curene® 442 | Anderson Development Company | PUR-Ester/TDI | Andur |
| Elvax® 3135XZ | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Petrotene® PP A3 G40 HF CNZ0207 PH356 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Thermec N™ 4314T1H | Technical Polymers, LLC | PPA | Thermec N™ |