LNP™ LUBRICOMP™ LL004C compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2w0gtf_LNP-LUBRICOMP-LL004C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant, Clean Compounding System. Also known as: LNP* LUBRICOMP* Compound LL-4040 CCS Product reorder name: LL004C |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.3 | % | |
| Across Flow : 24 hr | 1.9 | % | |
| Water Absorption (24 hr, 50% RH) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2900 | MPa | ASTM D638 |
| -- | 3070 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 74.5 | MPa | ASTM D638 |
| Yield | 73.0 | MPa | ISO 527-2 |
| Break | 69.6 | MPa | ASTM D638 |
| Break | 69.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.8 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2 |
| Break | 23 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2960 | MPa | ASTM D790 |
| -- | 3320 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 117 | MPa | ASTM D790 |
| -- | 118 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.52 | ||
| vs. Itself - Static | 0.43 | ||
| Wear Factor - Washer | 128 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 3 | 91 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.00 | J | ASTM D3763 |
| -- | 1.00 | J | ISO 6603-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 150 FV20 EV10 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| SEETEC LLDPE UC404 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| OxyVinyls® 450F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| TECHNYL® B 216 V30 GREY 2472 CF | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |
| Sylvin 802-100 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |