Vyncolit® X613
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y1Ovc3_Vyncolit-X613.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® X613 is a glass fiber and glass beads reinforced phenolic molding compound with high mechanical and thermal properties and excellent electrical insulation properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Apparent Density | 0.64 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.35 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ISO 62 |
| Post Shrinkage | 0.090 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.6 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.80 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 12000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 190 | MPa | ISO 178 |
| Compressive Stress | 260 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 3.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 213 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 1.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 5.5E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+13 | ohms | IEC 60093 |
| Volume Resistivity | 7.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 17 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Injection Time: 2 to 8 secHold Time: 1 to 5 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP261 | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| Shandong PA1212 Reinforced Nylon 1212 | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Cheng Yu FRV | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| EMERGE™ PC/ABS 7560 | Trinseo | PC+ABS | EMERGE™ |
| Polifor® C 8 GRIGIO 7222 | SO.F.TER. SPA | PP Copolymer | Polifor® |