Order Products : sales@su-jiao.com
Hostacom PC072-3 natural
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2qbr3o_Hostacom-PC072-3-natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass coupled PP- homopolymer. Low flow, high stiffness, low CLTE and outstanding LTHA values. Low creep under load at elevated temperatures. The product is designed for injection molding of washing machine parts and is available in natural color. Good hot water and detergent resistance. UL listing in all colors including RTI and compliance with UL 2157. It is not intended for medical, pharmaceutical and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238, ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.30 to 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 6400 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 90.0 | MPa | ASTM D638 |
| Yield, 23°C | 85.0 | MPa | ISO 527-2/50 |
| Break | 80.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 6000 | MPa | ASTM D790 |
| Secant | 5400 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 85 | J/m | |
| 23°C | 100 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 148 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ISO 306/A50 |
| -- | 130 | °C | ISO 306/B50 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm, ALL | HB | ||
| 1.50 mm, ALL | HB | ||
| 3.00 mm, ALL | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 138789 EG | RTP Company | PP, Unspecified | RTP |
| RTP 1000 TFE 15 | RTP Company | PBT | RTP |
| SUMILITE® EL-3762 | Sumitomo Bakelite Co., Ltd. | Epoxy | SUMILITE® |
| KYOCERA KE-850SH | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| MAJORIS EB810 | AD majoris | PP, Unspecified | MAJORIS |