RAMOFIN PPH343T4BK11
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2qZClw_RAMOFIN-PPH343T4BK11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% MINERAL FILLED, UV STABILIZED,HEAT RESISTANT POLYPROPYLENE FOR INJECTION MOLDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.0 to 1.4 | % | |
| -- | 1.0 to 1.4 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 25 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 55.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.8 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 51 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 134 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 82.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 154 | °C | ASTM D1525, ISO 306 |
| Melting Temperature | 168 | °C | ISO 11357-3, ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 22 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 225 | °C | |
| Front Temperature | 205 to 230 | °C | |
| Mold Temperature | 30.0 to 65.0 | °C | |
| Injection Pressure | 70.0 to 105 | MPa | |
| Holding Pressure | 35.0 to 70.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 6115 HS | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| Durez® 23570 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Karina SILVER COLOR CONCENTRATE 47/9-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Luranyl® HT 220 E | ROMIRA GmbH | PPE+Nylon 66 | Luranyl® |
| Petrothene® NA952 | LyondellBasell Industries | LDPE | Petrothene® |