Shuman PS 810
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Shuman Plastics, Inc. |
| Trademark: | Shuman PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zD480Y_Shuman-PS-810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYSTYRENE HIGH IMPACT 810 BLACK OFFERS THIS COMBINATION OF PROPERTIES:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 4.0 to 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 30.4 | MPa | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.2 | °C | ASTM D1525 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 204 to 227 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 to 227 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALGLASS H 07 S 40 G | RIALTI Srl | PP Homopolymer | RIALGLASS |
| DJSilicone NE-7180 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Flexalloy® 13-U14996A-52NT | Teknor Apex Company | PVC, Flexible | Flexalloy® |
| Geon™ Vinyl Flexible Y126 White 317 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Kumho PS GP 125E | Korea Kumho Petrochemical Co., Ltd. | PS (GPPS) | Kumho PS |