SD POLYCA™ IM-401-18
| Category: | PC , Polycarbonate |
| Manufacturer: | Sumika Styron Polycarbonate Limited |
| Trademark: | SD POLYCA™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2pccsV_SDPOLYCAIM40118.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SD POLYCA™ IM 400 series show high impact resistance at cold temperature. This series are suitable for housing of cell phone and other mobile equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 59.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 120 | % | ASTM D638 |
| Fracture | 110 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2130 | MPa | ASTM D790 |
| -- | 2240 | MPa | ISO 178 |
| Flexural Strength | 88.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 55 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 133 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 128 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 124 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.4 mm | V-2 | UL 94 | |
| 3.0 mm | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 A | RTP Company | Nylon 6 | RTP |
| POYAD PA211 | Pooya Polymer Tehran | Polyolefin, Unspecified | POYAD |
| YUNGSOX® PP 3554 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Nypol® PA A3 G25 NTLA010 NR342 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| PERLER® N09H0000B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |