Edgetek™ PK-30CF/000 FCR BK
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2oOb57_Edgetek-PK-30CF-000-FCR-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek®The engineering thermoplastic polymer product portfolio includes a series of standard and customizable high-performance materials. The combination includes high-temperature resistant materials for high-temperature working environments, and high-modulus/structural materials for load-bearing, high-strength applications and flame-retardant products. These polymers are made by mixing engineering thermoplastic resins with different reinforcing additives, such as carbon fiber, glass fiber and glass beads. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.050 - 0.20 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr, 3.18 mm | 0.050 | % | ASTM D570 |
| Saturation | 0.13 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 25000 | MPa | ASTM D638 |
| Tensile Strength 2(Break, 23°C) | 240 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 22000 | MPa | ASTM D790 |
| Flexural Strength | 360 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 325 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+5 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 350 - 390 | °C | |
| Mold Temperature | 170 - 190 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 8T | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Shandong PA610 GYEHVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 610 | Shandong PA610 |
| Yanshan PE 8200B | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| NORYL™ 6850C resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| Plaslube® PA6/6 AF10 HS L | Techmer Engineered Solutions | Nylon 66 | Plaslube® |