ACCUTECH™ HP0339W30L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7u4I1z_ACCUTECH-HP0339W30L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0339W30L1 is a polypropylene homopolymer (PP Homopoly) product containing 30% wollastonite (casio3). It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 32.0 | MPa | ASTM D638 |
| Fracture | 26.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 15 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 42.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 28 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 125 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 77.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorRx® ABS-0500NB | LTL Color Compounders, Inc. | ABS | ColorRx® |
| ENVIRON® ENV39-NC400 | ENVIROPLAS®, Inc. | PC+PBT | ENVIRON® |
| KEBAFORM® C 130.2 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| LNP™ LUBRICOMP™ MX06404 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |
| Durethan® DP AKV 50 HR H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |