Petrothene® NA143
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2hSO2H_Petrothene-NA143.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA 143 is a series of homopolymer resins for blown film. Applications include stiff liners. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 1.91 mm) | 11.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 23.4 | MPa | |
| TD : Yield, 32 µm | 17.2 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm | 300 | % | |
| TD : Break, 32 µm | 500 | % | |
| Dart Drop Impact (32 µm) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 380 | g | |
| TD : 32 µm | 200 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm) | 70 | ASTM D2457 | |
| Haze (31.8 µm) | 6.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Type IV, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RODRUN LC-5050GM | UNITIKA Plastics Division | LCP | RODRUN |
| SAN 124 | Trinseo | SAN | SAN |
| GECET™ F-300 | Fagerdala USA Inc. | PS (EPS) | GECET™ |
| Globalene® 7233N | Lee Chang Yung Chemical Industry Corp. | PP Impact Copolymer | Globalene® |
| Optix® CA-1000 I | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |