VICOTE® F814
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICOTE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gu8cD_VICOTE-F814.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VICOTE F814 has been specifically formulated to provide a resilient coating with high wear and abrasion resistance on ferrous and non-ferrous metals such as carbon and cast steel. These properties are retained at high temperatures where other coatings would potentially fail. Typical properties are high continuous use temperature of 280°C, excellent wear, abrasion and cut through resistance at these high temperatures combined with excellent chemical resistance. VICOTE dispersions have a low level of extractables and are inherently flame retardant. Contact Victrex plc for further details. VICOTE F814 dispersions are aqueous based however there are small amounts of solvents present. Refer to the appropriate MSDS sheet for details. The VICTREX® PEEK polymer contained in the VICOTE dispersions like other non-coating grades of VICTREX PEEK polymer are thermoplastic in nature and exhibit flow above the melt temperature. When processed using the correct guidelines the coatings will exhibit the excellent properties that VICTREX PEEK polymer is renowned for. For further information consult the Victrex Chemical Resistance Data sheets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (25°C) | 1.05 | g/cm³ | ISO 2811 |
| pH | 10.0 | Internal Method | |
| Viscosity (25°C) | 1.0 | min | ISO 2431 |
| Weight - Solids | 37 | % | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cross Hatch Adhesion 1 | ISO 2409 | ||
| Aluminum | 0 | ||
| Mild Steel | 0 | ||
| Stainless Steel | 0 | ||
| Direct Impact 2 | ISO 6272 | ||
| Height | 100.00 | cm | |
| Indentation depth | 0.50 | cm | |
| Weight | 2000 | g | |
| Konig Hardness (40.0 to 50.0 µm) | 2.4 | min | ISO 1522 |
| Theory Volume Solids | 28 | % |
| Mechanical | Nominal Value | Test Method | |
|---|---|---|---|
| Coefficient of Friction 3 | 0.54 | ASTM G133 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 280 | °C | |
| Melting Temperature 4 | 372 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Rating 0 to 5 |
| 2 . | Part 1 |
| 3 . | Using 250N Load, µm @ 10 min |
| 4 . | Peak |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3L HP UV | BASF Corporation | Nylon 66 | Ultramid® |
| HANWHA LLDPE 3322 | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| Idemitsu PS SEHI-110 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| Karina OCHER PVC COMPOUND 810-37/3-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9067-70 White 1275 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |